TYVcure EPL15
TYVcure EPL15 is a two-component epoxy coating system developed for repairing and renovating drains and sewage pipes, suitable for impregnation of liners/hoses and can be cured at both ambient and high temperatures.
Composition
TYVcure EPL15 resin consists of two liquid components:
- A component: epoxy containing blend
- B component: amine containing blend with special odor
Properties
- ambient cure
- quick cure (hot cure either warm air or steam)
- high mechanical properties
- excellent chemical resistance
- adheres to PVC, concrete, steel
Liquid Component Technical Data
| Name | Value | Unit |
|---|
| Density of 'a' component | 1.2 ± 0.1 | g/cm3 |
| Viscosity of 'a' component | 2500 ± 200 | mPas |
| Density of 'b' component | 1.0 ± 0.1 | g/cm3 |
| Viscosity of 'b' component | 600 ± 100 | mPas |
| Density of mixture | 1.1 ± 0.1 | g/cm3 |
| Viscosity of mixture | 2300 ± 250 | mPas |
Hardened Resin Technical Data
| Name | Value | Unit |
|---|
| Young’s modulus | > 3200 | MPa |
| Tensile strength | > 40 | MPa |
| Elongation at break | > 1 | % |
| Flexural modulus | > 3200 | MPa |
| Flexural strength | > 100 | MPa |
| Compression strength | > 140 | MPa |
| Shore-d hardness | > 80 | Shore-D |
| Glass-transition temperature | > 80 | °C |
Chemical Resistance
| Chemical | Result | Chemical | Result | Chemical | Result |
|---|
| Normal petrol | 5 | Super petrol | 5 | CaCl2- saturated | 5 |
| Diesel | 5 | Acetic acid 10% | 5 | Acetic acid 20% | 5 |
| Ethanol | 5 | Oil | 5 | Phosphoric acid 10% | 5 |
| H2O2 30% | 1 | H2O2 5% | 5 | H2SO4 10% | 5 |
| H2SO4 20% | 5 | H2SO4 40% | 5 | HCl 10% | 5 |
| HCl 37% | 5 | HNO3 10% | 5 | HNO3 20% | 5 |
| HNO3 40% | 5 | IPA | 5 | MgCl2- saturated | 5 |
| NaCl 20% | 5 | NaOH 10% | 5 | NaOH 30% | 5 |
| NaOH 50% | 5 | Lactic acid 10% | 5 | Toluol | 5 |
TYVcure EPL20
TYVcure EPL20 is a two-component epoxy coating system developed for repairing and renovating drains and sewage pipes. The system is suited for the impregnation of liners/hoses and can be cured at both ambient and high temperatures, specifically designed for short sections or cold ambient temperatures.
Composition
TYVcure EPL20 resin consists of two liquid components:
- A component: epoxy containing blend
- B component: amine containing blend with special odor
Properties
- ambient cure
- low viscosity
- quick cure (hot cure either warm air or steam)
- high mechanical properties
- excellent chemical resistance
- adheres to PVC, concrete, steel
Liquid Component Technical Data
| Name | Value | Unit |
|---|
| Density of 'a' component | 1.2 ± 0.1 | g/cm3 |
| Viscosity of 'a' component | 2500 ± 200 | mPas |
| Density of 'b' component | 1.0 ± 0.1 | g/cm3 |
| Viscosity of 'b' component | 90 ± 15 | mPas |
| Density of mixture | 1.1 ± 0.1 | g/cm3 |
| Viscosity of mixture | 1200 ± 150 | mPas |
Hardened Resin Technical Data
| Name | Value | Unit |
|---|
| Young’s modulus | > 3200 | MPa |
| Tensile strength | > 40 | MPa |
| Elongation at break | > 1 | % |
| Flexural modulus | > 3200 | MPa |
| Flexural strength | > 100 | MPa |
| Compression strength | > 150 | MPa |
| Shore-d hardness | > 80 | Shore-D |
| Glass-transition temperature | > 80 | °C |
Chemical Resistance
| Chemical | Result | Chemical | Result | Chemical | Result |
|---|
| Normal petrol | 4 | Super petrol | 5 | CaCl2- saturated | 5 |
| Diesel | 5 | Acetic acid 10% | 5 | Acetic acid 20% | 4 |
| Ethanol | 5 | Oil | 5 | Phosphoric acid 10% | 5 |
| H2O2 30% | 1 | H2O2 5% | 5 | H2SO4 10% | 5 |
| H2SO4 20% | 4 | H2SO4 40% | 5 | HCl 10% | 5 |
| HCl 37% | 4 | HNO3 10% | 5 | HNO3 20% | 5 |
| HNO3 40% | 5 | IPA | 5 | MgCl2- saturated | 5 |
| NaCl 20% | 5 | NaOH 10% | 5 | NaOH 30% | 5 |
| NaOH 50% | 5 | Lactic acid 10% | 5 | Toluol | 5 |
TYVcure EPL30
TYVcure EPL30 is a two-component epoxy coating system developed for repairing and renovating drains and sewage pipes, suitable for impregnation of liners/hoses, designed for short to medium sections. It can be cured at both ambient and high temperatures.
Composition
TYVcure EPL30 resin consists of two liquid components:
- A component: epoxy containing blend
- B component: amine containing blend with special odor
Properties
- ambient cure
- quick cure (hot cure either warm air or steam)
- high mechanical properties
- good chemical resistance
- adheres to PVC, concrete, steel
Liquid Component Technical Data
| Name | Value | Unit |
|---|
| Density of 'a' component | 1.2 ± 0.1 | g/cm3 |
| Viscosity of 'a' component | 2500 ± 200 | mPas |
| Density of 'b' component | 1.0 ± 0.1 | g/cm3 |
| Viscosity of 'b' component | 750 ± 100 | mPas |
| Density of mixture | 1.1 ± 0.1 | g/cm3 |
| Viscosity of mixture | 2100 ± 200 | mPas |
Hardened Resin Technical Data
| Name | Value | Unit |
|---|
| Young’s modulus | > 3000 | MPa |
| Tensile strength | > 50 | MPa |
| Elongation at break | > 2 | % |
| Flexural modulus | > 2800 | MPa |
| Flexural strength | > 80 | MPa |
| Compression strength | > 150 | MPa |
| Shore-d hardness | > 80 | Shore-D |
| Glass-transition temperature | > 85 | °C |
Chemical Resistance
| Chemical | Result | Chemical | Result | Chemical | Result |
|---|
| Normal petrol | 5 | Super petrol | 5 | CaCl2- saturated | 5 |
| Diesel | 4 | Acetic acid 10% | 5 | Acetic acid 20% | 4 |
| Ethanol | 5 | Oil | 5 | Phosphoric acid 10% | 5 |
| H2O2 30% | 1 | H2O2 5% | 3 | H2SO4 10% | 3 |
| H2SO4 20% | 3 | H2SO4 40% | 5 | HCl 10% | 5 |
| HCl 37% | 5 | HNO3 10% | 5 | HNO3 20% | 3 |
| HNO3 40% | 5 | IPA | 5 | MgCl2- saturated | 4 |
| NaCl 20% | 5 | NaOH 10% | 5 | NaOH 30% | 5 |
| NaOH 50% | 5 | Lactic acid 10% | 5 | Toluol | 3 |
TYVcure EPL60
TYVcure EPL60 is a two-component epoxy coating system developed for repairing and renovating drains and sewage pipes. The system is suited for the impregnation of liners/hoses and can be cured at both ambient and high temperatures, designed specifically for medium length sections.
Composition
TYVcure EPL60 resin consists of two liquid components:
- A component: epoxy containing blend
- B component: amine containing blend with special odor
Properties
- hot cure either warm air or steam
- good mechanical properties
- good chemical resistance
- adheres to PVC, concrete, steel
Liquid Component Technical Data
| Name | Value | Unit |
|---|
| Density of 'a' component | 1.2 ± 0.1 | g/cm3 |
| Viscosity of 'a' component | 5500 ± 500 | mPas |
| Density of 'b' component | 1.0 ± 0.1 | g/cm3 |
| Viscosity of 'b' component | 250 ± 50 | mPas |
| Density of mixture | 1.1 ± 0.1 | g/cm3 |
| Viscosity of mixture | 2600 ± 400 | mPas |
Hardened Resin Technical Data
| Name | Value | Unit |
|---|
| Young’s modulus | > 2800 | MPa |
| Tensile strength | > 45 | MPa |
| Elongation at break | > 1.5 | % |
| Flexural modulus | > 2800 | MPa |
| Flexural strength | > 90 | MPa |
| Compression strength | > 130 | MPa |
| Shore-d hardness | > 80 | Shore-D |
| Glass-transition temperature | > 90 | °C |
Chemical Resistance
| Chemical | Result | Chemical | Result | Chemical | Result |
|---|
| Normal petrol | 5 | Super petrol | 5 | CaCl2- saturated | 5 |
| Diesel | 5 | Acetic acid 10% | 5 | Acetic acid 20% | 1 |
| Ethanol | 5 | Oil | 5 | Phosphoric acid 10% | 1 |
| H2O2 30% | 1 | H2O2 5% | 4 | H2SO4 10% | 4 |
| H2SO4 20% | 3 | H2SO4 40% | 5 | HCl 10% | 5 |
| HCl 37% | 1 | HNO3 10% | 5 | HNO3 20% | 2 |
| HNO3 40% | 5 | IPA | 5 | MgCl2- saturated | 5 |
| NaCl 20% | 5 | NaOH 10% | 5 | NaOH 30% | 5 |
| NaOH 50% | 5 | Lactic acid 10% | 5 | Toluol | 5 |
TYVcure EPL90
TYVcure EPL90 is a two-component epoxy coating system developed for repairing and renovating drains and sewage pipes. The resin is suited for the impregnation of liners/hoses and can be cured at both ambient and high temperatures, designed specifically for long sections.
Composition
TYVcure EPL90 resin consists of two liquid components:
- A component: epoxy containing blend
- B component: amine containing blend with special odor
Properties
- hot cure either warm air or steam
- low viscosity
- good mechanical properties
- good chemical resistance
- adheres to PVC, concrete, steel
Liquid Component Technical Data
| Name | Value | Unit |
|---|
| Density of 'a' component | 1.2 ± 0.1 | g/cm3 |
| Viscosity of 'a' component | 2600 ± 300 | mPas |
| Density of 'b' component | 1.0 ± 0.1 | g/cm3 |
| Viscosity of 'b' component | 40 ± 20 | mPas |
| Density of mixture | 1.1 ± 0.1 | g/cm3 |
| Viscosity of mixture | 1000 ± 200 | mPas |
Hardened Resin Technical Data
| Name | Value | Unit |
|---|
| Young’s modulus | > 2600 | MPa |
| Tensile strength | > 40 | MPa |
| Elongation at break | > 1.5 | % |
| Flexural modulus | > 2800 | MPa |
| Flexural strength | > 80 | MPa |
| Compression strength | > 150 | MPa |
| Shore-d hardness | > 80 | Shore-D |
| Glass-transition temperature | > 85 | °C |
Chemical Resistance
| Chemical | Result | Chemical | Result | Chemical | Result |
|---|
| Normal petrol | 5 | Super petrol | 4 | CaCl2- saturated | 5 |
| Diesel | 5 | Acetic acid 10% | 5 | Acetic acid 20% | 3 |
| Ethanol | 5 | Oil | 5 | Phosphoric acid 10% | 4 |
| H2O2 30% | 1 | H2O2 5% | 5 | H2SO4 10% | 3 |
| H2SO4 20% | 4 | H2SO4 40% | 5 | HCl 10% | 5 |
| HCl 37% | 4 | HNO3 10% | 5 | HNO3 20% | 3 |
| HNO3 40% | 5 | IPA | 5 | MgCl2- saturated | 5 |
| NaCl 20% | 5 | NaOH 10% | 5 | NaOH 30% | 5 |
| NaOH 50% | 5 | Lactic acid 10% | 5 | Toluol | 5 |
TYVcure EPLT6
TYVcure EPLT6 is a two-component epoxy coating system developed for repairing and renovating drains and sewage pipes. The resin is suited for the impregnation of liners/hoses and can be cured at both ambient and high temperatures, designed specifically for extra-long sections or high ambient temperatures.
Composition
TYVcure EPLT6 resin consists of two liquid components:
- A component: epoxy containing blend
- B component: amine containing blend with special odor
Properties
- more than 6 hours pot life
- hot cure either warm air or steam
- low viscosity
- good mechanical properties
- good chemical resistance
- adheres to PVC, concrete, steel
Liquid Component Technical Data
| Name | Value | Unit |
|---|
| Density of 'a' component | 1.2 ± 0.1 | g/cm3 |
| Viscosity of 'a' component | 5500 ± 500 | mPas |
| Density of 'b' component | 1.0 ± 0.1 | g/cm3 |
| Viscosity of 'b' component | 20 ± 5 | mPas |
| Density of mixture | 1.1 ± 0.1 | g/cm3 |
| Viscosity of mixture | 500 ± 100 | mPas |
Hardened Resin Technical Data
| Name | Value | Unit |
|---|
| Young’s modulus | > 2600 | MPa |
| Tensile strength | > 50 | MPa |
| Elongation at break | > 2 | % |
| Flexural modulus | > 2800 | MPa |
| Flexural strength | > 70 | MPa |
| Compression strength | > 140 | MPa |
| Shore-d hardness | > 80 | Shore-D |
| Glass-transition temperature | > 80 | °C |
Chemical Resistance
| Chemical | Result | Chemical | Result | Chemical | Result |
|---|
| Normal petrol | 5 | Super petrol | 5 | CaCl2- saturated | 5 |
| Diesel | 5 | Acetic acid 10% | 1 | Acetic acid 20% | 1 |
| Ethanol | 3 | Oil | 5 | Phosphoric acid 10% | 5 |
| H2O2 30% | 1 | H2O2 5% | 4 | H2SO4 10% | 5 |
| H2SO4 20% | 5 | H2SO4 40% | 5 | HCl 10% | 5 |
| HCl 37% | 5 | HNO3 10% | 5 | HNO3 20% | 5 |
| HNO3 40% | 3 | IPA | 5 | MgCl2- saturated | 5 |
| NaCl 20% | 5 | NaOH 10% | 5 | NaOH 30% | 5 |
| NaOH 50% | 5 | Lactic acid 10% | 2 | Toluol | 2 |
TYVcure EPLT24
TYVcure EPLT24 is a two-component epoxy coating system developed for repairing and renovating drains and sewage pipes, suited for the impregnation of liners/hoses. It is designed for extra-long sections or high ambient temperatures and can be cured at both ambient and high temperatures.
Composition
TYVcure EPLT24 resin consists of two liquid components:
- A component: epoxy containing blend
- B component: amine containing blend with special odor
Properties
- extreme long potlife (> 24 hours)
- quick cure (~2 hours) at 80 °C
- low viscosity
- high Tg
- good mechanical properties
- outstanding chemical resistance
- adheres to PVC, concrete, steel
Liquid Component Technical Data
| Name | Value | Unit |
|---|
| Density of 'a' component | 1.2 ± 0.1 | g/cm3 |
| Viscosity of 'a' component | 2800 ± 400 | mPas |
| Density of 'b' component | 1.0 ± 0.1 | g/cm3 |
| Viscosity of 'b' component | 20 ± 5 | mPas |
| Density of mixture | 1.1 ± 0.1 | g/cm3 |
| Viscosity of mixture | 800 ± 200 | mPas |
Hardened Resin Technical Data
| Name | Value | Unit |
|---|
| Young’s modulus | > 2800 | MPa |
| Tensile strength | > 25 | MPa |
| Elongation at break | > 0.5 | % |
| Flexural modulus | > 2500 | MPa |
| Flexural strength | > 70 | MPa |
| Compression strength | > 150 | MPa |
| Shore-d hardness | > 80 | Shore-D |
| Glass-transition temperature | > 120 | °C |
Chemical Resistance
| Chemical | Result | Chemical | Result | Chemical | Result |
|---|
| Normal petrol | 5 | Super petrol | 5 | CaCl2- saturated | 5 |
| Diesel | 5 | Acetic acid 10% | 5 | Acetic acid 20% | 5 |
| Ethanol | 5 | Oil | 5 | Phosphoric acid 10% | 5 |
| H2O2 30% | 5 | H2O2 5% | 5 | H2SO4 10% | 5 |
| H2SO4 20% | 5 | H2SO4 40% | 5 | HCl 10% | 5 |
| HCl 37% | 5 | HNO3 10% | 5 | HNO3 20% | 5 |
| HNO3 40% | 5 | IPA | 5 | MgCl2- saturated | 5 |
| NaCl 20% | 5 | NaOH 10% | 5 | NaOH 30% | 5 |
| NaOH 50% | 5 | Lactic acid 10% | 5 | Toluol | 5 |